秋霞黄色网 I 免费av一级片 I 久久国产网站 I 动漫美女被人操 I 高清黄色大片 I 免费不卡的av I 欧美极品少妇xxxxⅹ免费视频 I 日本黄大片在线观看 I 巨乳中文字幕在线观看 I 在线免费av观看 I 亚洲黄色片在线观看 I 黄色片视频在线观看 I 让领导弄进去了的娇妻 I av人体 I 欧美 日韩 国产 激情 I 美女调教vk I 日韩第一视频 I 在线不卡的av I 日本视频网站在线观看 I 精品在线视频一区二区三区 I 美女狂揉下部 I 亚洲日本va中文字幕久久 I 网红主播av I 酒店大战丝袜高跟鞋人妻 I 国内精品 中文字幕 I 久播影院在线观看 I 青娱乐超碰在线91 I www.成人深夜激情 I 亚洲精品电影久久久 I 婷婷久久综合九色综合88 I 国产精品亚洲а∨天堂123bt I 尤物视频在线观看网站 I 亚洲成aⅴ人最新无码 I 日韩三级黄色毛片 I 久久人搡人人玩人妻精品 I heyzo少妇av精东影视 I 丰满五十六十老熟女hd I 曰本色欧美视频在线 I 亚洲交换

 

（1） The top coat foams after baking

 

Scrape off the bubbles after the top coat bubbles, and see which layer the bubbles are on. If the bubbles appear in the primer layer, the putty and the primer are well combined, and the substrate treatment may not be in place; after scraping the bubbles, it is found that there is a layer of primer on both the putty and the substrate, so it may be that the primer is too thick or the primer is not completely dry.

 

（2） Pinholes and pits appear after baking

 

First of all, whether the quality problem of atomic ash itself caused pinholes was considered. Secondly, if the quality of the putty is qualified, the pinholes are generally due to the poor scraping and grinding technology of the putty, and the sand holes are not handled properly. In addition, in the process of coating and scraping, if the coating tool is not selected properly, pinholes will also be caused.

 

（3） "Prickly heat" after baking the top coat

 

First, the climate is too humid, and the water absorption rate of atomic ash is too large. The polished atomic ash absorbs a considerable amount of water. Before the water volatilizes, the top coat is sprayed. A small amount of water is sealed under the paint film. Once heated, the water volume expands rapidly, breaking through the paint film to form "prickly heat".

 

Second, the water absorption of atomic ash is qualified. After hot air drying, the top coat is sprayed, and "prickly heat" appears after baking. Then, it is possible that after spraying the top coat, the solvent will enter the drying room before the solvent is fully volatilized. In this way, as the surface of the topcoat is closed quickly, the residual solvent has to break through the paint film to form "prickly heat". Of course, it may be the quality of the topcoat, or the polarity of the solvent does not match the topcoat, resulting in "prickly heat".

 

（4） Cracking of putty or primer

 

In the paint repair area, the putty filled area or primer layer cracks, resulting in the cracking of the top coat.

 

reason:

 

① The thickness of the putty layer or intermediate primer layer is too thick, and the drying time between each layer is not sufficient, which makes the surface of the putty layer or intermediate coat primer layer dry and the bottom layer soft, resulting in the cracking of the putty layer or intermediate primer layer. Therefore, in the process of putty scraping or primer spraying, thin layer and multiple construction should be adopted, and enough drying time should be reserved according to the climatic conditions.

 

② The transition zone between the primer coat of putty or intermediate coat and the old paint layer, i.e. the periphery of feather edge, is not fully treated, which leads to the incomplete bonding and cracking of the putty coating. 600 sandpaper should be used to avoid the solvent being brought into the deep scraping layer of the lower layer.

 

③ The thinner used in the primer does not meet the requirements, resulting in the primer layer is not easy to dry or excessive shrinkage and cracking.

 

Correction method:

 

Grind the cracked area thoroughly, scrape AFR and spray primer and topcoat, and pay attention to leave enough drying time between coatings.